Effect of soldering on shear bond strength of porcelain fused to metal. (In vitro study)
الناشر \ المحرر \ الكاتب (Author / Editor / Publisher)
احمد غانم مهدي الهلال
Citation Information
احمد,غانم,مهدي,الهلال ,Effect of soldering on shear bond strength of porcelain fused to metal. (In vitro study) , Time 5/11/2011 6:35:51 PM : كلية طب الاسنان
وصف الابستركت (Abstract)
A thesis Submitted to the council of the college of Dentistry at the University of Baghdad, in partial fulfillment of the requirements of the degree of master science in conservative dent.
الوصف الكامل (Full Abstract)
partial fulfiment of master degree in conservative dentistry---- council of college of dentistry --- baghdad universityEffect of soldering on shear bond strength of porcelain fused to metal. (In vitro study) Ahmed G. Mehdi B.D.S., M.Sc. Adel F. Ibrahim B.D.S., M.Sc.
ABSTRACT: Background:The insertion of metal frameworks is critical during the fabrication of metal-ceramic restorations to ensure adequate fit to the abutments. When fit is inadequate, sectioning of the metal framework is required, which is then soldered in the dental laboratory.Materials and Methods: Forty cylindrical metal (Ni-Cr alloy) specimens were prepared; it has 8 mm diameter and 3 mm height. Half of these specimens were made in such a way so that it has perforation in the center of 1mm in diameter; the later group is then soldered. All the samples were oxidized, and then sandblasted with aluminum oxide. The ceramic material (vita VMK 95) was applied, the final thickness of ceramic was 1.5 mm, and then the samples was finished and glazed. Half of the soldered and half of non soldered samples were stored in distilled water for one week, and then shear bond strength was evaluated for all samples. After the testing, all samples were inspected visually and microscopically to detect the nature of failure.Results and Conclusion:The result revealed that the intact specimens (non soldered) has higher shear bond strength values than the soldered specimens, and there is no influence of the water storage on shear bond strength for both groups. The visual and microscopical observations show that the non soldered groups have higher percentage of cohesive failure than soldered groups which has higher percentage of adhesive failure.Key words:Soldering, Porcelain fused to metal, shear bond test.